Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 84
Page 153
... increase in the crack growth rate at the more protective potentials due to higher hydrogen contents , similar to those shown in Fig 7. A further increase in growth rate occurred in the biologically active test environment where SRB were ...
... increase in the crack growth rate at the more protective potentials due to higher hydrogen contents , similar to those shown in Fig 7. A further increase in growth rate occurred in the biologically active test environment where SRB were ...
Page 184
... increase of strength with very small in- plane gaps . Lalani and Bolt ( 1990 ) therefore proposed two modifiers for ... increase lessens as y increases . · The increase of the capacity ratio with C is again thought to be caused by the ...
... increase of strength with very small in- plane gaps . Lalani and Bolt ( 1990 ) therefore proposed two modifiers for ... increase lessens as y increases . · The increase of the capacity ratio with C is again thought to be caused by the ...
Page 450
... increase plastic strain . An apparent increase in the weld metal strength is observed , and increases in applied load can be achieved after the initial yielding of the undermatched weld . For example , for a thin plate wide enough to ...
... increase plastic strain . An apparent increase in the weld metal strength is observed , and increases in applied load can be achieved after the initial yielding of the undermatched weld . For example , for a thin plate wide enough to ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength