Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 84
Page 164
... indicated that austenitic steels could have poorer fatigue strengths than C - Mn steels . As seen in the figure some of the points for austenitic types fall below the design line . However , most results are above the Class E curve ...
... indicated that austenitic steels could have poorer fatigue strengths than C - Mn steels . As seen in the figure some of the points for austenitic types fall below the design line . However , most results are above the Class E curve ...
Page 532
... ( indicated by arrows in Figure 7 ) confirms that the solidifi- cation indeed began with the precipitation of primary austenite ( Sudgen and Bhadeshia , 1988 ) . Analyses using 3903 15KV X100 100PM WD39 Figure 5. Fracture Surface of a ...
... ( indicated by arrows in Figure 7 ) confirms that the solidifi- cation indeed began with the precipitation of primary austenite ( Sudgen and Bhadeshia , 1988 ) . Analyses using 3903 15KV X100 100PM WD39 Figure 5. Fracture Surface of a ...
Page 584
... indicated a value of 3.2mm . Nevertheless these experiments have indicated that wet welds with an uncritical ( lower embrittlement ) are achievable . Further investigations are under progress . e . Full scale Scallop test . For the ...
... indicated a value of 3.2mm . Nevertheless these experiments have indicated that wet welds with an uncritical ( lower embrittlement ) are achievable . Further investigations are under progress . e . Full scale Scallop test . For the ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength