Page 112
ན ། Table4 Conditions and Results of Experimental Model Joint for Residual. Residual Stress ( MPa ) 300 200 100 0000 0 -100 -200 - : Axial Stress : Hoop Stress Residual Stress ( MPa ) 300 200 : Axial Stress Hoop Stress 100 O -100 -200 ...
ན ། Table4 Conditions and Results of Experimental Model Joint for Residual. Residual Stress ( MPa ) 300 200 100 0000 0 -100 -200 - : Axial Stress : Hoop Stress Residual Stress ( MPa ) 300 200 : Axial Stress Hoop Stress 100 O -100 -200 ...
Page 114
Table4 Conditions and Results of Experimental Model Joint for Residual Stress Measurement Model No. Joint Type JIS ... Residual Stress --- 114.
Table4 Conditions and Results of Experimental Model Joint for Residual Stress Measurement Model No. Joint Type JIS ... Residual Stress --- 114.
Page 542
... residual stresses interact with the stresses that oc- cur due to the external load and the stress singularity at the crack tip . There are also great differences in the residual stress dis- tributions at the weld bead . The influence of ...
... residual stresses interact with the stresses that oc- cur due to the external load and the stress singularity at the crack tip . There are also great differences in the residual stress dis- tributions at the weld bead . The influence of ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength