... STEEL WELDMENTS There are far fewer S - N data for welded stainless steel than for C - Mn steels , particularly in the high cycle life regime and at ambient temperature . Furthermore , there is little information on the corrosion ...
... STEEL WELDMENTS There are far fewer S - N data for welded stainless steel than for C - Mn steels , particularly in the high cycle life regime and at ambient temperature . Furthermore , there is little information on the corrosion ...
Page 273
... steels for tubular applications will be blocked ( 3.4 ) DEVELOPMENT IMPACT OF STEEL MECHANICAL PROPERTIES ON In recent studies at Cranfield considerable effort has been made to examine the changes which have occurred over the years in steel ...
... steels for tubular applications will be blocked ( 3.4 ) DEVELOPMENT IMPACT OF STEEL MECHANICAL PROPERTIES ON In recent studies at Cranfield considerable effort has been made to examine the changes which have occurred over the years in steel ...
Page 367
... steel production practices , particularly reduced carbon levels , altemative grain size control , and strengthening methods and improved steel cleanliness . Such steels obviously show different deformation behaviour to older type high ...
... steel production practices , particularly reduced carbon levels , altemative grain size control , and strengthening methods and improved steel cleanliness . Such steels obviously show different deformation behaviour to older type high ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength