Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 90
Page 224
... surface of the component such that it flows in a " thin uniform skin " perpendicular to the plane of the surface flaw . The major difference between the two techniques is that ACPD relies on measurements of the surface electric field in ...
... surface of the component such that it flows in a " thin uniform skin " perpendicular to the plane of the surface flaw . The major difference between the two techniques is that ACPD relies on measurements of the surface electric field in ...
Page 331
... surfaces were measured with a travelling microscope ( 4X magnification ) . Comparisons of these profiles with the crack depths predicted from potential drop showed that the deepest points of surface cracks and edge cracks were generally ...
... surfaces were measured with a travelling microscope ( 4X magnification ) . Comparisons of these profiles with the crack depths predicted from potential drop showed that the deepest points of surface cracks and edge cracks were generally ...
Page 360
... surface of plate ( mm ) FIG.7 LOCATION DEPENDENCE OF AVERAGE FERRITE GRAIN SIZES IN CROSS - SECTION OF DEVELOPED ... Surface average grain size in thickness - direction is shown in Fig . 7 , as an example . In the surface layer , the ...
... surface of plate ( mm ) FIG.7 LOCATION DEPENDENCE OF AVERAGE FERRITE GRAIN SIZES IN CROSS - SECTION OF DEVELOPED ... Surface average grain size in thickness - direction is shown in Fig . 7 , as an example . In the surface layer , the ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength