Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 83
Page 93
... results of large scale ( curved wide plate ) tests on thin wall pipelines ( thickness < 12,7 mm ) have been compared with small scale ( Charpy V notch impact and CTOD ) test results . The result of the comparisons show that ( a ) the ...
... results of large scale ( curved wide plate ) tests on thin wall pipelines ( thickness < 12,7 mm ) have been compared with small scale ( Charpy V notch impact and CTOD ) test results . The result of the comparisons show that ( a ) the ...
Page 210
... test results . When the results of these tests are finally incorporated into the design codes , designers will have more realistic and more reliable fatigue design curves for tubular connections at their disposal . In this study , all ...
... test results . When the results of these tests are finally incorporated into the design codes , designers will have more realistic and more reliable fatigue design curves for tubular connections at their disposal . In this study , all ...
Page 360
... TEST RESULTS FOR DEVELOPED STEEL PLATE OF 25mm IN THICKNESS . 0.25mmR , 45deg . 2mm depth Surface average grain size ... Results of tensile tests are shown in Table 2. Tensile properties are fully satisfied the NK ( Nippon Kaiji Kyokai ) ...
... TEST RESULTS FOR DEVELOPED STEEL PLATE OF 25mm IN THICKNESS . 0.25mmR , 45deg . 2mm depth Surface average grain size ... Results of tensile tests are shown in Table 2. Tensile properties are fully satisfied the NK ( Nippon Kaiji Kyokai ) ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength