Page 4
... Thickness Effect A penalty on life for increasing joint thickness was first introduced in the Third Edition guidance [ 13 ] . It is now widely accepted that for joints with thicknesses exceeding the basic thickness a correction factor ...
... Thickness Effect A penalty on life for increasing joint thickness was first introduced in the Third Edition guidance [ 13 ] . It is now widely accepted that for joints with thicknesses exceeding the basic thickness a correction factor ...
Page 9
... thickness ratio , t , of 1 yielded a thickness exponent of 0.29 for m = 3 . Various assessments of the thickness effect are presented in [ 39-41 ] . It is recognised that the thickness effect is more complex than the representation in ...
... thickness ratio , t , of 1 yielded a thickness exponent of 0.29 for m = 3 . Various assessments of the thickness effect are presented in [ 39-41 ] . It is recognised that the thickness effect is more complex than the representation in ...
Page 206
... thickness below say 22 mm . Wingerde ( 1992 ) advocated that the beneficial thickness effect is real down to thicknesses in the range of 4 mm , although with a somewhat different thickness dependency than the one given in Equation ( 2 ) ...
... thickness below say 22 mm . Wingerde ( 1992 ) advocated that the beneficial thickness effect is real down to thicknesses in the range of 4 mm , although with a somewhat different thickness dependency than the one given in Equation ( 2 ) ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength