Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 69
Page 209
... tested in air and tubular joints tested in sea water with cathodic protection are the same at long fatigue lives . At short fatigue lives , tubular joints tested in sea ... Tubular Joints Dimitrakis, Frederick V Lawrence, and William C Mohr.
... tested in air and tubular joints tested in sea water with cathodic protection are the same at long fatigue lives . At short fatigue lives , tubular joints tested in sea ... Tubular Joints Dimitrakis, Frederick V Lawrence, and William C Mohr.
Page 212
... test data for tubular joints tested in sea water with cathodic protection lie above the DOE S - N design curve : see Fig . 10 . 3.3.3 Determination of Environmental Life Reduction Factors for Tubular Joints Tested In Sea Water Under ...
... test data for tubular joints tested in sea water with cathodic protection lie above the DOE S - N design curve : see Fig . 10 . 3.3.3 Determination of Environmental Life Reduction Factors for Tubular Joints Tested In Sea Water Under ...
Page 213
... Screening Criteria for Tubular Joints Tested. Only a small number of brace failures ( 22 ) pass the screening criteria . No effect of weldment size was observed when the limited number of brace failures were evaluated . The best - fit ...
... Screening Criteria for Tubular Joints Tested. Only a small number of brace failures ( 22 ) pass the screening criteria . No effect of weldment size was observed when the limited number of brace failures were evaluated . The best - fit ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength