... values in the centre greater than those at the surface ( Pook 1994b ) . The average through thickness value for plane strain is closer to the two dimensional solution than the plane stress average . Plane strain conditions were ...
... values in the centre greater than those at the surface ( Pook 1994b ) . The average through thickness value for plane strain is closer to the two dimensional solution than the plane stress average . Plane strain conditions were ...
Page 237
... values are positive indicates that the edge value is always lower than the centre value . The grooved specimens however , show a transition from where the root value is higher ; decreasing in magnitude ; to one where the root value is ...
... values are positive indicates that the edge value is always lower than the centre value . The grooved specimens however , show a transition from where the root value is higher ; decreasing in magnitude ; to one where the root value is ...
Page 266
... values ) are compared with values obtained for this geometry from various other sources . Around the intersection , the stress concentration factor distributions exhibit the same overall trend as the shell model . However , at the ...
... values ) are compared with values obtained for this geometry from various other sources . Around the intersection , the stress concentration factor distributions exhibit the same overall trend as the shell model . However , at the ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength