Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 70
Page 93
... wide plate ) tests on thin wall pipelines ( thickness < 12,7 mm ) have been compared with small scale ( Charpy V notch impact and CTOD ) test results . The result of the comparisons show that ( a ) the Charpy V notch impact test can be ...
... wide plate ) tests on thin wall pipelines ( thickness < 12,7 mm ) have been compared with small scale ( Charpy V notch impact and CTOD ) test results . The result of the comparisons show that ( a ) the Charpy V notch impact test can be ...
Page 94
... Wide plate test performance criterion The non - dimensional wide plate failure stresses ( expressed as the failure stress to pipe metal yield strength ratio ) and / or the wide plate failure strains can be used to derive the required ...
... Wide plate test performance criterion The non - dimensional wide plate failure stresses ( expressed as the failure stress to pipe metal yield strength ratio ) and / or the wide plate failure strains can be used to derive the required ...
Page 333
... WIDE ) ; EXPERIMENT AND MODEL PREDICTIONS . Figure 4 illustrates the crack depth ( as measured by the potential drop ... wide test specimens than along the unground weld toes of the 203 mm wide test specimens . As a result , the aspect ...
... WIDE ) ; EXPERIMENT AND MODEL PREDICTIONS . Figure 4 illustrates the crack depth ( as measured by the potential drop ... wide test specimens than along the unground weld toes of the 203 mm wide test specimens . As a result , the aspect ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength