... yield strength , for example 60 % of yield strength under normal loading or 80 % under severe loading ( 24.25 ) . Traditionally , design was undertaken on an elastic basis and the application of such an approach ensured that tensile ...
... yield strength , for example 60 % of yield strength under normal loading or 80 % under severe loading ( 24.25 ) . Traditionally , design was undertaken on an elastic basis and the application of such an approach ensured that tensile ...
Page 367
... yield ratio ( YR ) is plotted against the mean value of yield strength for both quenched and tempered and TMCP steels of plate thickness 50mm . Although there is considerable variation for steels of similar yield strength , overall the ...
... yield ratio ( YR ) is plotted against the mean value of yield strength for both quenched and tempered and TMCP steels of plate thickness 50mm . Although there is considerable variation for steels of similar yield strength , overall the ...
Page 369
... Yield Yield Charpy Strength Ratio Impart NWV AVTI Cr Mo Ni BS4360 : 50D A Normalised 0.20 ( old ) 1.35 355 B BS7191 355EMZ Normalised 0.11 ( modern ) 1.50 0.40 「 3333 0.3 0.015 0016 0.028 / - 0.02 / · · . 5 : 3 ( MPa ) ( YR = YP ...
... Yield Yield Charpy Strength Ratio Impart NWV AVTI Cr Mo Ni BS4360 : 50D A Normalised 0.20 ( old ) 1.35 355 B BS7191 355EMZ Normalised 0.11 ( modern ) 1.50 0.40 「 3333 0.3 0.015 0016 0.028 / - 0.02 / · · . 5 : 3 ( MPa ) ( YR = YP ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength