Deformation and Fracture Mechanics of Engineering MaterialsUpdated to reflect recent developments in our understanding of deformation and fracture processes in structural materials. This completely revised reference includes new sections on isostress analysis, modulus of rupture, creep fracture micromechanicsms, and many more. |
From inside the book
Results 1-3 of 34
Page 378
... environment include stress corrosion cracking ( SCC ) , hydrogen embrittlement ( HE ) , and liquid metal embrittlement ( LME ) . The subject of fatigue and corrosion fatigue is examined in Chapter ... Environment Assisted Cracking (EAC)
... environment include stress corrosion cracking ( SCC ) , hydrogen embrittlement ( HE ) , and liquid metal embrittlement ( LME ) . The subject of fatigue and corrosion fatigue is examined in Chapter ... Environment Assisted Cracking (EAC)
Page 504
... environment . For exam- ple , the harmful effects of a 3.5 % saline solution ... assisted cracking does occur below KIEAC when the arrested crack is ... cracking , Kiscc , has been redefined by the more general term for environment ...
... environment . For exam- ple , the harmful effects of a 3.5 % saline solution ... assisted cracking does occur below KIEAC when the arrested crack is ... cracking , Kiscc , has been redefined by the more general term for environment ...
Page 564
... crack reached a depth and length of 0.64 cm and 1.42 cm , respectively , could have been due to the onset of static environment assisted cracking at a stress intensity where the cracking rate became independent of the K level ( i.e. ...
... crack reached a depth and length of 0.64 cm and 1.42 cm , respectively , could have been due to the onset of static environment assisted cracking at a stress intensity where the cracking rate became independent of the K level ( i.e. ...
Other editions - View all
Common terms and phrases
alloy aluminum alloy American Society applied stress associated ASTM STP atoms behavior brittle Burgers vector Chapter Charpy component crack growth rate crack length crack tip craze crystal crystalline cycles decreasing depends ductility effect elastic embrittlement engineering environment assisted cracking example failure FIGURE flaw fracture mechanics fracture surface fracture toughness given grain boundary hydrogen initial KIEAC lattice load Materials from copyright metallurgical microstructure modulus MPa Vm notch occur orientation parameter plane strain plane stress plastic deformation plastic zone plate polymer properties R. W. Hertzberg region relationship relative Reprinted with permission response result sample screw dislocation Section sensitivity shear stress shown in Fig slip plane slip systems specimen stacking fault energy strain hardening strain rate stress concentration stress intensity factor stress level stress-strain curve striation Table tensile test temperature Testing and Materials texture thickness Trans transition temperature twin values yield strength