Deformation and Fracture Mechanics of Engineering MaterialsUpdated to reflect recent developments in our understanding of deformation and fracture processes in structural materials. This completely revised reference includes new sections on isostress analysis, modulus of rupture, creep fracture micromechanicsms, and many more. |
From inside the book
Results 1-3 of 28
Page 134
... rupture tests usually provide only one datum - the rupture life tR . Rupture life information is sometimes used in the design of engineering components that will have a service life up to 105 hours . An example of such data is given in ...
... rupture tests usually provide only one datum - the rupture life tR . Rupture life information is sometimes used in the design of engineering components that will have a service life up to 105 hours . An example of such data is given in ...
Page 166
... rupture life response toward the more time - consuming low - temperature , long rupture life regime . It is generally found that such extrapolations to longer time conditions are reasonably accurate at higher stress levels because a ...
... rupture life response toward the more time - consuming low - temperature , long rupture life regime . It is generally found that such extrapolations to longer time conditions are reasonably accurate at higher stress levels because a ...
Page 168
... rupture data for different alloys much in the same manner as the Larson - Miller ( L - M ) parameter . Reasonably good results have been obtained with this parameter in correlating high temperature data of relatively pure metals10 ( Fig ...
... rupture data for different alloys much in the same manner as the Larson - Miller ( L - M ) parameter . Reasonably good results have been obtained with this parameter in correlating high temperature data of relatively pure metals10 ( Fig ...
Other editions - View all
Common terms and phrases
alloy aluminum alloy American Society applied stress associated ASTM STP atoms behavior brittle Burgers vector Chapter Charpy component crack growth rate crack length crack tip craze crystal crystalline cycles decreasing depends ductility effect elastic embrittlement engineering environment assisted cracking example failure FIGURE flaw fracture mechanics fracture surface fracture toughness given grain boundary hydrogen initial KIEAC lattice load Materials from copyright metallurgical microstructure modulus MPa Vm notch occur orientation parameter plane strain plane stress plastic deformation plastic zone plate polymer properties R. W. Hertzberg region relationship relative Reprinted with permission response result sample screw dislocation Section sensitivity shear stress shown in Fig slip plane slip systems specimen stacking fault energy strain hardening strain rate stress concentration stress intensity factor stress level stress-strain curve striation Table tensile test temperature Testing and Materials texture thickness Trans transition temperature twin values yield strength