Mechanical metallurgy |
From inside the book
Results 1-3 of 82
Page 208
Moreover, the presence of second-phase particles in the continuous matrix
phase results in localized internal stresses which modify the plastic properties of
the continuous phase. Many factors must be considered for a complete
understanding ...
Moreover, the presence of second-phase particles in the continuous matrix
phase results in localized internal stresses which modify the plastic properties of
the continuous phase. Many factors must be considered for a complete
understanding ...
Page 316
The other property that is measured in the notch tensile test is the reduction of
area at the notch. As strength, hardness, or some metallurgical variable
restricting plastic flow increases, the metal at the root of the notch is less able to
flow, and ...
The other property that is measured in the notch tensile test is the reduction of
area at the notch. As strength, hardness, or some metallurgical variable
restricting plastic flow increases, the metal at the root of the notch is less able to
flow, and ...
Page 322
Slack quenching results in tensile properties which are somewhat poorer than
those obtained with a completely tempered martensitic structure. The yield
strength and the reduction of area are generally most affected, while impact
strength can ...
Slack quenching results in tensile properties which are somewhat poorer than
those obtained with a completely tempered martensitic structure. The yield
strength and the reduction of area are generally most affected, while impact
strength can ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Stress and Strain Relationships for Elastic Behavior | 18 |
from Elastic Strains 213 Strain Energy 214 Anisotropy | 46 |
Metallurgical Fundamentals | 101 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
alloy angle annealed ASTM atoms axes axis behavior billet brittle fracture Burgers vector cold-worked components compression constant crack creep cycles decrease determined diameter direction dislocation line ductile edge dislocation elastic elongation embrittlement energy engineering equation extrusion factor failure fatigue limit fibers Figure flow curve flow stress force forging friction given grain boundaries hot-working hydrostatic increase indentation lattice length load machining martensite material matrix maximum measured mechanical metallurgical Metals Park modulus necking notch occurs particles percent plane strain plane-strain plastic deformation plastic strain pressure produce properties ratio recrystallization reduction region residual stresses rolling screw dislocation shear stress sheet shown in Fig slip plane slip systems Society for Metals specimen steel strain hardening strain rate stress-strain curve structure surface temperature tensile strength tensile stress tension test tensor thickness tool torsion Trans usually velocity workpiece yield strength yield stress