... Table 1. Three - dimen- sional finite element fracture mechanics calculations were carried out to determine the stress intensity factors for the measured crack profiles , and the results were compared with stress intensities back ...
... Table 1. Three - dimen- sional finite element fracture mechanics calculations were carried out to determine the stress intensity factors for the measured crack profiles , and the results were compared with stress intensities back ...
Page 272
... Table 2 was continuously cast , and control - rolled to a 50 mm thick plate followed by TMCP and tempering . Here TMCP refers to direct quenching . Tempering was performed at 550 ° C . MECHANICAL PROPERTIES OF PLATE Table 3 shows the ...
... Table 2 was continuously cast , and control - rolled to a 50 mm thick plate followed by TMCP and tempering . Here TMCP refers to direct quenching . Tempering was performed at 550 ° C . MECHANICAL PROPERTIES OF PLATE Table 3 shows the ...
Page 650
... Table 3. The welding direction was parallel to the final rolling direction of plate . Welding was carried out with attention to keep the straightness of fusion line . Table 1 Chemical composition of steel used ( wt . % ) C SI 0.08 0.30 ...
... Table 3. The welding direction was parallel to the final rolling direction of plate . Welding was carried out with attention to keep the straightness of fusion line . Table 1 Chemical composition of steel used ( wt . % ) C SI 0.08 0.30 ...
Contents
THICKNESS EFFECTS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics Offshore Structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength