Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 76
Page 311
... composition was considered unsuitable for welding this strength of steel . Only 1 Ni Consumable Development The use of the 1 % Ni 0.25 % Mo composition for achieving the required weld metal strength and toughness properties for the ...
... composition was considered unsuitable for welding this strength of steel . Only 1 Ni Consumable Development The use of the 1 % Ni 0.25 % Mo composition for achieving the required weld metal strength and toughness properties for the ...
Page 353
... Composition of Commercial Grades of Cast HSLA Steel COMPOSITION. ABSTRACT High - Strength low - alloy ( HSLA ) cast steels have been developed with excellent strength , toughness and weldability similar to the widely used wrought HSLA ...
... Composition of Commercial Grades of Cast HSLA Steel COMPOSITION. ABSTRACT High - Strength low - alloy ( HSLA ) cast steels have been developed with excellent strength , toughness and weldability similar to the widely used wrought HSLA ...
Page 354
Chemical Composition of Commercial Grades of Cast HSLA Steel COMPOSITION , % 1,20-2,00 0,03-0,07 1,20-2,00 0,03-0,07 1,20-2,00 0,03-0,07 100 Figure 7. Cast HSLA steel nodes ( Armitage ,. % Mn CE = % C + 6 + % Cr + % Mo + % V 5 + % Cu + ...
Chemical Composition of Commercial Grades of Cast HSLA Steel COMPOSITION , % 1,20-2,00 0,03-0,07 1,20-2,00 0,03-0,07 1,20-2,00 0,03-0,07 100 Figure 7. Cast HSLA steel nodes ( Armitage ,. % Mn CE = % C + 6 + % Cr + % Mo + % V 5 + % Cu + ...
Contents
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Thickness Weld Profile and Initial Flaw Considerations for Tubular Joints | 39 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
adhesion strength alloy aluminum analysis applied Arctic Engineering austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord composite Conference on Offshore corrosion fatigue crack depth crack front crack growth rate crack initiation crack propagation crevice corrosion CTOD defects developed energy equation experimental fabrication fatigue crack growth fatigue strength ferrite Figure finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm levels line spring load material mechanical properties Mechanics and Arctic method microstructure notch Offshore Mechanics offshore structures parameter pipe pitting pitting corrosion plate thickness predicted PWHT ratio reduced S-N curves shown in Fig solution specimens strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values wall thickness weld metal weld profile weld toe weldability welded joints yield strength