... Constant Amplitude Loading In Air The crack initiation lives N , and endurances N of T - joints with attachments and base plates of equal thickness ranging from 16 to 103 mm ( specimen types A to E in Fig . 1 ) are shown in Fig . 2 ...
... Constant Amplitude Loading In Air The crack initiation lives N , and endurances N of T - joints with attachments and base plates of equal thickness ranging from 16 to 103 mm ( specimen types A to E in Fig . 1 ) are shown in Fig . 2 ...
Page 435
... constant amplitude tests and to the results presented in the literature . From Fig . 9 it can be seen that all spectrum test results lie within a normal scatter band close to the constant amplitude reference curve for structural steels ...
... constant amplitude tests and to the results presented in the literature . From Fig . 9 it can be seen that all spectrum test results lie within a normal scatter band close to the constant amplitude reference curve for structural steels ...
Page 520
... constant amplitude ( CA ) loading conditions and these results show a trend of decreasing threshold value with increasing R ratio . The implication from the data is that because high R ratio cycles will exist in a variable amplitude ...
... constant amplitude ( CA ) loading conditions and these results show a trend of decreasing threshold value with increasing R ratio . The implication from the data is that because high R ratio cycles will exist in a variable amplitude ...
Contents
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Thickness Weld Profile and Initial Flaw Considerations for Tubular Joints | 39 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
adhesion strength alloy aluminum analysis applied Arctic Engineering austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord composite Conference on Offshore corrosion fatigue crack depth crack front crack growth rate crack initiation crack propagation crevice corrosion CTOD defects developed energy equation experimental fabrication fatigue crack growth fatigue strength ferrite Figure finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm levels line spring load material mechanical properties Mechanics and Arctic method microstructure notch Offshore Mechanics offshore structures parameter pipe pitting pitting corrosion plate thickness predicted PWHT ratio reduced S-N curves shown in Fig solution specimens strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values wall thickness weld metal weld profile weld toe weldability welded joints yield strength