... Growth P1. ABSTRACT The fatigue of offshore tubular joints normally occurs under very complex random loading . Predicting the rate of damage accumu- lation in these joints is difficult and consequently extensive fatigue crack growth ...
... Growth P1. ABSTRACT The fatigue of offshore tubular joints normally occurs under very complex random loading . Predicting the rate of damage accumu- lation in these joints is difficult and consequently extensive fatigue crack growth ...
Page 397
... fatigue crack growth rate of the materials due to sea wave and sea current was developed . The field tests of fatigue crack growth measurements using Ni - Cr - Mo - V ocean structural steels were performed in cathodic protec- tion and ...
... fatigue crack growth rate of the materials due to sea wave and sea current was developed . The field tests of fatigue crack growth measurements using Ni - Cr - Mo - V ocean structural steels were performed in cathodic protec- tion and ...
Page 726
Table 1. Relevant Parameters for Fatigue Crack Propagation in Girth Welded Joints Figure 2. Loading Histories ... GROWTH IN GIRTH WELDED JOINTS 2.1 Fatigue Crack Growth Prediction Model The probabilistic analysis of the uncertainties ...
Table 1. Relevant Parameters for Fatigue Crack Propagation in Girth Welded Joints Figure 2. Loading Histories ... GROWTH IN GIRTH WELDED JOINTS 2.1 Fatigue Crack Growth Prediction Model The probabilistic analysis of the uncertainties ...
Contents
THICKNESS EFFECTS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics Offshore Structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength