Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 69
Page 173
... fracture toughness behaviour . The alpha - beta annealed samples exhibit a higher toughness compared with the original mill annealed condition , reaching , after 4 hours at 900oC a similar level to beta heat treated and air cooled ...
... fracture toughness behaviour . The alpha - beta annealed samples exhibit a higher toughness compared with the original mill annealed condition , reaching , after 4 hours at 900oC a similar level to beta heat treated and air cooled ...
Page 719
... fracture toughness data necessary for the reliability analysis of weldments ( section 1 ) , Defect distribution after NDI considering the detectability of NDT ( section 2 ) , 3 Analysis of failure probability for welded joints with a ...
... fracture toughness data necessary for the reliability analysis of weldments ( section 1 ) , Defect distribution after NDI considering the detectability of NDT ( section 2 ) , 3 Analysis of failure probability for welded joints with a ...
Page 724
... fracture mechanics parameter along the crack front , CTOD test results can ... Toughness of Structural Steels Prior to Production , Proc . 7th Int . Conf ... Fracture Toughness of Steel Welds , IIW Doc . X - 1135-87 , ( 1987 ) , ( to be ...
... fracture mechanics parameter along the crack front , CTOD test results can ... Toughness of Structural Steels Prior to Production , Proc . 7th Int . Conf ... Fracture Toughness of Steel Welds , IIW Doc . X - 1135-87 , ( 1987 ) , ( to be ...
Contents
THICKNESS EFFECTS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics Offshore Structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength