Page 34
... influence of the thick- ness of the attachment and for the influence of the fatigue life . The other results are only adjusted for the influence of the fatigue life since for those tests the t / T is unity . The applied formula for this ...
... influence of the thick- ness of the attachment and for the influence of the fatigue life . The other results are only adjusted for the influence of the fatigue life since for those tests the t / T is unity . The applied formula for this ...
Page 35
... INFLUENCE OF WELD PROFILE In considering the weld profile a clear distinc- tion has to be made between the overall weld angle and the shape of the weld toe . It is obvious that the shape of the weld toe ( radius , local angle and ...
... INFLUENCE OF WELD PROFILE In considering the weld profile a clear distinc- tion has to be made between the overall weld angle and the shape of the weld toe . It is obvious that the shape of the weld toe ( radius , local angle and ...
Page 443
... Influence of Cathodic Over - Protection In seawater with cathodic over - protection , total fatigue life re- duction factors for the pipe - plate specimens , PP7 and PP8 - tested at 240 or 160 MPa hot - spot stress , were 4.17 and 3.33 ...
... Influence of Cathodic Over - Protection In seawater with cathodic over - protection , total fatigue life re- duction factors for the pipe - plate specimens , PP7 and PP8 - tested at 240 or 160 MPa hot - spot stress , were 4.17 and 3.33 ...
Contents
THICKNESS EFFECTS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics Offshore Structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength