Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 23
Page 208
... pitting index base metals . It also significantly improved with an increase in the pitting index of the base metal . However , pitting corrosion performance appears to be independent of the welding method . Girth weld joints of high ...
... pitting index base metals . It also significantly improved with an increase in the pitting index of the base metal . However , pitting corrosion performance appears to be independent of the welding method . Girth weld joints of high ...
Page 208
... pitting index base metals . It also significantly improved with an increase in the pitting index of the base metal . However , pitting corrosion performance appears to be independent of the welding method . Girth weld joints of high ...
... pitting index base metals . It also significantly improved with an increase in the pitting index of the base metal . However , pitting corrosion performance appears to be independent of the welding method . Girth weld joints of high ...
Page 212
... Pitting C1 -SCC H , S - SCC Condition 30 ° C , 10 % FeC1,6,0 , 24h 3 100 ° C , 40 % CaCl2 , pH = 6.5 500h , U - bend ... Pitting BM ** GW C1 -SCC BM GW BM H2S - SCC 0.8SMYS No pitting No pitting No pitting No pitting No cracking No ...
... Pitting C1 -SCC H , S - SCC Condition 30 ° C , 10 % FeC1,6,0 , 24h 3 100 ° C , 40 % CaCl2 , pH = 6.5 500h , U - bend ... Pitting BM ** GW C1 -SCC BM GW BM H2S - SCC 0.8SMYS No pitting No pitting No pitting No pitting No cracking No ...
Contents
THICKNESS EFFECTS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics Offshore Structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength