Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 21
Page 208
... pitting index base metals . It also significantly improved with an increase in the pitting index of the base metal . However , pitting corrosion performance appears to be independent of the welding method . Girth weld joints of high ...
... pitting index base metals . It also significantly improved with an increase in the pitting index of the base metal . However , pitting corrosion performance appears to be independent of the welding method . Girth weld joints of high ...
Page 212
... Pitting BM ** GW C1 -SCC BM GW No pitting No pitting No pitting No pitting No pitting No pitting No pitting No cracking No cracking No cracking No cracking No cracking No cracking No cracking No cracking No failure No failure No failure No ...
... Pitting BM ** GW C1 -SCC BM GW No pitting No pitting No pitting No pitting No pitting No pitting No pitting No cracking No cracking No cracking No cracking No cracking No cracking No cracking No cracking No failure No failure No failure No ...
Page 224
... pitting index Cr + 3,3Mo + 30N Fig . 4 Critical pitting temperatures ( CPT , above ) and critical crevice temperatures ( CCT , below ) of stainless steels and alloys tested in 1o w / o ferric chloride solution ( details see text ) ...
... pitting index Cr + 3,3Mo + 30N Fig . 4 Critical pitting temperatures ( CPT , above ) and critical crevice temperatures ( CCT , below ) of stainless steels and alloys tested in 1o w / o ferric chloride solution ( details see text ) ...
Contents
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Thickness Weld Profile and Initial Flaw Considerations for Tubular Joints | 39 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
adhesion strength alloy aluminum analysis applied Arctic Engineering austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord composite Conference on Offshore corrosion fatigue crack depth crack front crack growth rate crack initiation crack propagation crevice corrosion CTOD defects developed energy equation experimental fabrication fatigue crack growth fatigue strength ferrite Figure finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm levels line spring load material mechanical properties Mechanics and Arctic method microstructure notch Offshore Mechanics offshore structures parameter pipe pitting pitting corrosion plate thickness predicted PWHT ratio reduced S-N curves shown in Fig solution specimens strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values wall thickness weld metal weld profile weld toe weldability welded joints yield strength