As shown experimentally and by fracture mechancis analysis by Maddox ( 1987 ) the elastic stress Concentration at the weld toe of a transverse fillet weld depends the thickness of the attachment . The thickness effect may therefore be ...
As shown experimentally and by fracture mechancis analysis by Maddox ( 1987 ) the elastic stress Concentration at the weld toe of a transverse fillet weld depends the thickness of the attachment . The thickness effect may therefore be ...
Page 24
Fatigue lives were in the range 5 • 105 - 4 • 106 applied cycles . The load spectrum was truncated at 15 % of naximum stress range . In terms of a full spectrum the corresponding lives were 5 • 106 4 • 10 ' . The data are shown in Fig .
Fatigue lives were in the range 5 • 105 - 4 • 106 applied cycles . The load spectrum was truncated at 15 % of naximum stress range . In terms of a full spectrum the corresponding lives were 5 • 106 4 • 10 ' . The data are shown in Fig .
Page 730
It can be readily inferred that an inspection for defects deeper than 10 mm will not influence the future survival predictions until after 10 years , as shown in Figure 6 . Scatter diagrams of crack length and depth which would cause ...
It can be readily inferred that an inspection for defects deeper than 10 mm will not influence the future survival predictions until after 10 years , as shown in Figure 6 . Scatter diagrams of crack length and depth which would cause ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
THICKNESS EFFECTS | 1 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Thickness Weld Profile and Initial Flaw Considerations for Tubular Joints | 39 |
Copyright | |
46 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied base behaviour bending calculated carried compared composition concrete Conference constant corrosion crack growth CTOD curve cycles defect depth determined developed distribution effect element energy Engineering equation experimental fabrication factor failure fatigue crack Figure fracture function geometry given grade grain heat higher improved increase indicated influence initiation input inspection International length limited load lower material mean measured mechanical method microstructure normal notch observed obtained occur Offshore parameters performed pipe plate potential predicted present procedure production properties protection range ratio reduced region Research shown shows specimens standard steel strain strength stress stress intensity factor stress range structure surface Table temperature tensile thickness toughness tubular joints values weld metal weld toe welded joints wide plate yield strength
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1989 |
| Export Citation | BiBTeX EndNote RefMan |