... weld metal tension tests are not extensively used in qualification / production testing . The all weld metal test is normally made once . Since welding is a complicated process which can affect significantly the all weld metal ...
... weld metal tension tests are not extensively used in qualification / production testing . The all weld metal test is normally made once . Since welding is a complicated process which can affect significantly the all weld metal ...
Page 637
Valuation of weld metal matching . The valuation of the actual degree of weld metal yield strength overmatching was achieved by comparing the distributions of the weld and plate metal yield strengths with each other in Figures 9 through ...
Valuation of weld metal matching . The valuation of the actual degree of weld metal yield strength overmatching was achieved by comparing the distributions of the weld and plate metal yield strengths with each other in Figures 9 through ...
Page 638
... weld metal yield strength overmatching in 420/450 MPa yield strength steels without giving consideration to the plate metal's manufacturing process and the yield strength supply range . Further , the information con- tained in Figure 11 ...
... weld metal yield strength overmatching in 420/450 MPa yield strength steels without giving consideration to the plate metal's manufacturing process and the yield strength supply range . Further , the information con- tained in Figure 11 ...
Contents
THICKNESS EFFECTS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics Offshore Structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength