... Weld Profile at Constant Amplitude In The effects of reduced attachment thickness , and improved weld profile as per AWS D1.1 ( 1986 ) recommen- dations were examined in two exploratory series of tests using type F joints ( Fig . 1 ) ...
... Weld Profile at Constant Amplitude In The effects of reduced attachment thickness , and improved weld profile as per AWS D1.1 ( 1986 ) recommen- dations were examined in two exploratory series of tests using type F joints ( Fig . 1 ) ...
Page 36
... weld profile was considerably lower than that of the normal profile ( figure 16 ) . This means that if the same results are given with the nominal stress range plotted on the vertical axis a significant better fatigue behaviour of the ...
... weld profile was considerably lower than that of the normal profile ( figure 16 ) . This means that if the same results are given with the nominal stress range plotted on the vertical axis a significant better fatigue behaviour of the ...
Page 43
... weld profile control reduced the adverse thickness effect by about one - half . The example above was based on finite element solutions where the mesh remained constant , except along the surface of the weld . As the weld was made ...
... weld profile control reduced the adverse thickness effect by about one - half . The example above was based on finite element solutions where the mesh remained constant , except along the surface of the weld . As the weld was made ...
Contents
THICKNESS EFFECTS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics Offshore Structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength