Scattering from Polymers: Characterization by X-rays, Neutrons, and LightThis book reflects the recent progress made in the field of scattering in polymers. A wide range of scattering studies on different polymer systems, including block copolymers, semicrystalline polymers, complex fluids, multicomponent systems, polymeric surfaces, and polymer processing are included, as well as new experimental techniques and theoretical treatments. This volume provides a comprehensive reference for those researchers who need to know how scattering techniques can be used to tackle different polymer problems, and is ideal for graduate polymer scientists studying scattering techniques. |
From inside the book
Results 1-3 of 68
Page 43
... scattering patterns are recorded on image plates placed 1.8 m behind the sample . After exposing for 1 min the maximum recorded scattering intensity amounts to 60,000 counts . The geometry of the chosen semi transparent beam stop ...
... scattering patterns are recorded on image plates placed 1.8 m behind the sample . After exposing for 1 min the maximum recorded scattering intensity amounts to 60,000 counts . The geometry of the chosen semi transparent beam stop ...
Page 44
... scattering , he has proposed to analyze pro- jections , which can be extracted from the scattering patterns and reflect a longitudinal and a transverse structure , respectively . Following a concept of Ruland [ 7 , 8 ] , the re- sulting ...
... scattering , he has proposed to analyze pro- jections , which can be extracted from the scattering patterns and reflect a longitudinal and a transverse structure , respectively . Following a concept of Ruland [ 7 , 8 ] , the re- sulting ...
Page
... scattering ( SAXS ) profiles , first - order peak in- tensity , and domain ... patterns for aligned sample of SI - C1 at various temperatures , 480 , 483f ... scattering patterns for modified blend at deeper quench depth , 426f , 427f ...
... scattering ( SAXS ) profiles , first - order peak in- tensity , and domain ... patterns for aligned sample of SI - C1 at various temperatures , 480 , 483f ... scattering patterns for modified blend at deeper quench depth , 426f , 427f ...
Contents
Preface Xi | 11 |
Characteristics of SmallAngle Diffraction Data from Semicrystalline | 24 |
Block Crystallization in Model Triarm Star Block Copolymers | 28 |
Copyright | |
28 other sections not shown
Common terms and phrases
alignment American Chemical Society amorphous analysis annealing average beam behavior blends calculated Chem complexes concentration copolymer correlation function crystallization temperature decrease degree of crystallinity dependence detector differential scanning calorimetry diffraction diffusion distribution domain EMAA endotherm equation experimental experiments heating increase interactions interface isotactic isothermal isothermal crystallization lamellar stacks layer light scattering linear long period lyotropic Macromolecules measurements melting temperature micellar micelles microtubules molecular weight molecules neutron neutron scattering nucleation observed obtained orientation P(MAA/NIPAM parameters PEEK fractions Phys plot Pluronic poly(vinyl alcohol polyelectrolyte probes profiles quench reflections region rotator phase sample SAXS scanning scattering curve scattering intensity scattering patterns scattering peaks semicrystalline shear flow shear rate shown in Figure shows small angle solutions solvent spherulite structure factor surface surfactant synchrotron thermal thermotropic transition triclinic two-arm PEOs viscosity volume fraction WAXD WAXS width x-ray scattering