CORROSION FATIGUE BEHAVIOR OF TAR EPOXY RESIN COATED SHIP STRUCTURAL STEEL Akira Fushimi Faculty of Engineering , Tokyo University Tokyo , Japan 4 . 5 . Fatigue Strength Evaluation of Welded Joint. 1997 OMAE - Volume III , Materials ...
CORROSION FATIGUE BEHAVIOR OF TAR EPOXY RESIN COATED SHIP STRUCTURAL STEEL Akira Fushimi Faculty of Engineering , Tokyo University Tokyo , Japan 4 . 5 . Fatigue Strength Evaluation of Welded Joint. 1997 OMAE - Volume III , Materials ...
Page 150
... corrosion fatigue life is slightly observed in N , lower than 105 cycles . 600 Nominal stress range . AS ( MPa ) 500 400 AS - 2275 x Nf - 01759 300 200 888 ន ៖ ទ KA32 ( TMCP ) . Artificial sea water ( 298K ) 0.17Hz , R : 0.05 ...
... corrosion fatigue life is slightly observed in N , lower than 105 cycles . 600 Nominal stress range . AS ( MPa ) 500 400 AS - 2275 x Nf - 01759 300 200 888 ន ៖ ទ KA32 ( TMCP ) . Artificial sea water ( 298K ) 0.17Hz , R : 0.05 ...
Page 154
... corrosion fatigue strength in low stress and long life region are future problem to be solved . Based on the issue of this study it can be considered to be resonable to apply tar epoxy resin coating with about 200 μ m thickness for ...
... corrosion fatigue strength in low stress and long life region are future problem to be solved . Based on the issue of this study it can be considered to be resonable to apply tar epoxy resin coating with about 200 μ m thickness for ...
Contents
SPECTRAL MODELLING OF WAVES | 1 |
RISK ANALYSIS | 33 |
PROBABILISTIC MODELLING OF WAVES | 99 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis applied ASME assessment base metal bending brittle fracture calculated coefficient corrosion fatigue crack arrestability crack depth crack growth crack tip CTOD curve damage defects deformation dent Det Norske Veritas developed distribution dynamic earthquake effect energy Engineering equation estimated evaluated factor failure fatigue crack Figure fracture mechanics fracture toughness frequency function heat increase initiation inspection Japan maintenance martensitic material maximum mbar measured mechanical properties method notch observed obtained offshore structures OMAE parameters peening performed pipe plastic platform prediction pressure procedure ratio reliability response risers S-N curve safety sea water seismic shielding gas ship shown in Fig simulation single-sided welds specimens spectra spectrum statistical steel plate strain stress range surface Table temperature tensile toughness tubular underwater underwater welding vertical wave height Weibull distribution weld metal welded joints width yield strength yield stress