Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 16, Parts 2-3American Society of Mechanical Engineers, 1997 - Arctic regions |
From inside the book
Results 1-3 of 66
Page 197
... crack growth rate data in air. 1997 OMAE - - Volume III , Materials Engineering ASME 1997 ABSTRACT The importance of ... growth kinetics of such short cracks have been shown to be more rapid than those of long cracks ; however , it is ...
... crack growth rate data in air. 1997 OMAE - - Volume III , Materials Engineering ASME 1997 ABSTRACT The importance of ... growth kinetics of such short cracks have been shown to be more rapid than those of long cracks ; however , it is ...
Page 233
... crack depths greater than 10mm . The few crack depth readings available for specimen S3 meant that the crack growth rate had to be inferred using the secant method as opposed to the seven point method used for the other specimens ( ASTM ...
... crack depths greater than 10mm . The few crack depth readings available for specimen S3 meant that the crack growth rate had to be inferred using the secant method as opposed to the seven point method used for the other specimens ( ASTM ...
Page 259
... crack growth before fracture . CTOD testing at -10 ° C did not provide statistically significant characteristic values for the toughness , but it was demonstrated that brittle fracture initiation from CGHAZ could take place at CTOD ...
... crack growth before fracture . CTOD testing at -10 ° C did not provide statistically significant characteristic values for the toughness , but it was demonstrated that brittle fracture initiation from CGHAZ could take place at CTOD ...
Contents
SPECTRAL MODELLING OF WAVES | 1 |
RISK ANALYSIS | 33 |
PROBABILISTIC MODELLING OF WAVES | 99 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis applied ASME assessment base metal bending brittle fracture calculated coefficient corrosion fatigue crack arrestability crack depth crack growth crack tip CTOD curve damage defects deformation dent Det Norske Veritas developed distribution dynamic earthquake effect energy Engineering equation estimated evaluated factor failure fatigue crack Figure fracture mechanics fracture toughness frequency function heat increase initiation inspection Japan maintenance martensitic material maximum mbar measured mechanical properties method notch observed obtained offshore structures OMAE parameters peening performed pipe plastic platform prediction pressure procedure ratio reliability response risers S-N curve safety sea water seismic shielding gas ship shown in Fig simulation single-sided welds specimens spectra spectrum statistical steel plate strain stress range surface Table temperature tensile toughness tubular underwater underwater welding vertical wave height Weibull distribution weld metal welded joints width yield strength yield stress