Page 147
... effect of tar epoxy resin coating for improvement of corrosion fatigue life was not observed . The lower the stress level , an improving effect for corrosion fatigue life increased . An increase of corrosion fatigue life by tar epoxy ...
... effect of tar epoxy resin coating for improvement of corrosion fatigue life was not observed . The lower the stress level , an improving effect for corrosion fatigue life increased . An increase of corrosion fatigue life by tar epoxy ...
Page 263
... effect on stress distribution Effect of higher strength HAZ In a weldment , the HAZ property distribution is not uniform . From the weld thermal simulation results we have seen that different cooling rate will affect the properties of ...
... effect on stress distribution Effect of higher strength HAZ In a weldment , the HAZ property distribution is not uniform . From the weld thermal simulation results we have seen that different cooling rate will affect the properties of ...
Page 292
... effect . For the SM490- H ( II ) steel with lower fracture toughness , the stress elevation effect seems to be dominant to cause brittle fracture at a higher temperature . On the other hand , as for the SN490 ( II ) steel with superior ...
... effect . For the SM490- H ( II ) steel with lower fracture toughness , the stress elevation effect seems to be dominant to cause brittle fracture at a higher temperature . On the other hand , as for the SN490 ( II ) steel with superior ...
Contents
SPECTRAL MODELLING OF WAVES | 1 |
RISK ANALYSIS | 33 |
PROBABILISTIC MODELLING OF WAVES | 99 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis applied ASME assessment base metal bending brittle fracture calculated coefficient corrosion fatigue crack arrestability crack depth crack growth crack tip CTOD curve damage defects deformation dent Det Norske Veritas developed distribution dynamic earthquake effect energy Engineering equation estimated evaluated factor failure fatigue crack Figure fracture mechanics fracture toughness frequency function heat increase initiation inspection Japan maintenance martensitic material maximum mbar measured mechanical properties method notch observed obtained offshore structures OMAE parameters peening performed pipe plastic platform prediction pressure procedure ratio reliability response risers S-N curve safety sea water seismic shielding gas ship shown in Fig simulation single-sided welds specimens spectra spectrum statistical steel plate strain stress range surface Table temperature tensile toughness tubular underwater underwater welding vertical wave height Weibull distribution weld metal welded joints width yield strength yield stress