Fracture Resistance Evaluation of High Strength Structural Steel Components by Wide Plate Testing and Finite Element Analyses Mons Hauge Dept. of Fracture Mechanics and Materials Testing SINTEF Materials Technology Trondheim , Norway ...
Fracture Resistance Evaluation of High Strength Structural Steel Components by Wide Plate Testing and Finite Element Analyses Mons Hauge Dept. of Fracture Mechanics and Materials Testing SINTEF Materials Technology Trondheim , Norway ...
Page 259
... fracture . CTOD testing at -10 ° C did not provide statistically significant characteristic values for the toughness , but it was demonstrated that brittle fracture initiation from CGHAZ could take place at CTOD levels down to about 0.1 ...
... fracture . CTOD testing at -10 ° C did not provide statistically significant characteristic values for the toughness , but it was demonstrated that brittle fracture initiation from CGHAZ could take place at CTOD levels down to about 0.1 ...
Page 283
... fracture property of structural steels . 3D FE - analysis , taking account of the strain rate effect on the flow stress , figured out that the dynamic loading elevates a local stress near the notch tip to a large extent . This was ...
... fracture property of structural steels . 3D FE - analysis , taking account of the strain rate effect on the flow stress , figured out that the dynamic loading elevates a local stress near the notch tip to a large extent . This was ...
Contents
SPECTRAL MODELLING OF WAVES | 1 |
RISK ANALYSIS | 33 |
PROBABILISTIC MODELLING OF WAVES | 99 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis applied ASME assessment base metal bending brittle fracture calculated coefficient corrosion fatigue crack arrestability crack depth crack growth crack tip CTOD curve damage defects deformation dent Det Norske Veritas developed distribution dynamic earthquake effect energy Engineering equation estimated evaluated factor failure fatigue crack Figure fracture mechanics fracture toughness frequency function heat increase initiation inspection Japan maintenance martensitic material maximum mbar measured mechanical properties method notch observed obtained offshore structures OMAE parameters peening performed pipe plastic platform prediction pressure procedure ratio reliability response risers S-N curve safety sea water seismic shielding gas ship shown in Fig simulation single-sided welds specimens spectra spectrum statistical steel plate strain stress range surface Table temperature tensile toughness tubular underwater underwater welding vertical wave height Weibull distribution weld metal welded joints width yield strength yield stress