WELD JOINT FRACTURE TOUGHNESS OF NARROW GAP WELDED DISSIMILAR HSLA STEEL Arpad Treiber University of Maribor Faculty ... fracture toughness of joints provided by 85.
WELD JOINT FRACTURE TOUGHNESS OF NARROW GAP WELDED DISSIMILAR HSLA STEEL Arpad Treiber University of Maribor Faculty ... fracture toughness of joints provided by 85.
Page 88
... fracture toughness and Charpy toughness are the consequence of it . CONCLUSIONS An experimental programme to compare strength and toughness of mis - matched narrow gap weld joints produced on two HSLA steels in BM similar and dissimilar ...
... fracture toughness and Charpy toughness are the consequence of it . CONCLUSIONS An experimental programme to compare strength and toughness of mis - matched narrow gap weld joints produced on two HSLA steels in BM similar and dissimilar ...
Page 292
... fracture toughness , the stress elevation effect seems to be dominant to cause brittle fracture at a higher temperature . On the other hand , as for the SN490 ( II ) steel with superior toughness , the temperature rise effect is ...
... fracture toughness , the stress elevation effect seems to be dominant to cause brittle fracture at a higher temperature . On the other hand , as for the SN490 ( II ) steel with superior toughness , the temperature rise effect is ...
Contents
SPECTRAL MODELLING OF WAVES | 1 |
RISK ANALYSIS | 33 |
PROBABILISTIC MODELLING OF WAVES | 99 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis applied ASME assessment base metal bending brittle fracture calculated coefficient corrosion fatigue crack arrestability crack depth crack growth crack tip CTOD curve damage defects deformation dent Det Norske Veritas developed distribution dynamic earthquake effect energy Engineering equation estimated evaluated factor failure fatigue crack Figure fracture mechanics fracture toughness frequency function heat increase initiation inspection Japan maintenance martensitic material maximum mbar measured mechanical properties method notch observed obtained offshore structures OMAE parameters peening performed pipe plastic platform prediction pressure procedure ratio reliability response risers S-N curve safety sea water seismic shielding gas ship shown in Fig simulation single-sided welds specimens spectra spectrum statistical steel plate strain stress range surface Table temperature tensile toughness tubular underwater underwater welding vertical wave height Weibull distribution weld metal welded joints width yield strength yield stress