Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 16, Parts 2-3American Society of Mechanical Engineers, 1997 - Arctic regions |
From inside the book
Results 1-3 of 69
Page 115
... joints YR Fracture Side bend test YS TS Material ( MPa ) ( MPa ) ( % ) ( % ) position TIG welded metal 624 845 30 74 ... joint Table 4 SSC test results of welded joint Table 5 115.
... joints YR Fracture Side bend test YS TS Material ( MPa ) ( MPa ) ( % ) ( % ) position TIG welded metal 624 845 30 74 ... joint Table 4 SSC test results of welded joint Table 5 115.
Page 159
... joints [ 14 ] in which the welds were ground with grinders so as to result in Kw of around 2 . In this case , the joints with ground weld also locate near the lines of as - welded joints . When the best fit curve is extrapolated to Kw ...
... joints [ 14 ] in which the welds were ground with grinders so as to result in Kw of around 2 . In this case , the joints with ground weld also locate near the lines of as - welded joints . When the best fit curve is extrapolated to Kw ...
Page 319
... joints containing root defects would appear to be characterised by the Class F2 curve . Thus , the effect of these small defects is to reduce the fatigue life by a factor of approximately 2 . Although joints without defects show higher ...
... joints containing root defects would appear to be characterised by the Class F2 curve . Thus , the effect of these small defects is to reduce the fatigue life by a factor of approximately 2 . Although joints without defects show higher ...
Contents
SPECTRAL MODELLING OF WAVES | 1 |
RISK ANALYSIS | 33 |
PROBABILISTIC MODELLING OF WAVES | 99 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis applied ASME assessment base metal bending brittle fracture calculated coefficient corrosion fatigue crack arrestability crack depth crack growth crack tip CTOD curve damage defects deformation dent Det Norske Veritas developed distribution dynamic earthquake effect energy Engineering equation estimated evaluated factor failure fatigue crack Figure fracture mechanics fracture toughness frequency function heat increase initiation inspection Japan maintenance martensitic material maximum mbar measured mechanical properties method notch observed obtained offshore structures OMAE parameters peening performed pipe plastic platform prediction pressure procedure ratio reliability response risers S-N curve safety sea water seismic shielding gas ship shown in Fig simulation single-sided welds specimens spectra spectrum statistical steel plate strain stress range surface Table temperature tensile toughness tubular underwater underwater welding vertical wave height Weibull distribution weld metal welded joints width yield strength yield stress