Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 16, Parts 2-3American Society of Mechanical Engineers, 1997 - Arctic regions |
From inside the book
Results 1-3 of 64
Page 105
... welded joint with the weld metal of super duplex stainless steel . In this case ( Case II ) , the weld metal was almost even matching . In the case I the stress concentration was existed in the base metal near fusion line . On the other ...
... welded joint with the weld metal of super duplex stainless steel . In this case ( Case II ) , the weld metal was almost even matching . In the case I the stress concentration was existed in the base metal near fusion line . On the other ...
Page 115
... welded joints YR Fracture Side bend test YS TS Material ( MPa ) ( MPa ) ( % ) ( % ) position TIG welded metal 624 845 30 74 BM No crack MIG welded metal 597 856 30 70 BM No crack Base metal 634 827 34 77 The results of tensile and side ...
... welded joints YR Fracture Side bend test YS TS Material ( MPa ) ( MPa ) ( % ) ( % ) position TIG welded metal 624 845 30 74 BM No crack MIG welded metal 597 856 30 70 BM No crack Base metal 634 827 34 77 The results of tensile and side ...
Page 159
... joints [ 14 ] in which the welds were ground with grinders so as to result in Kw of around 2 . In this case , the joints with ground weld also locate near the lines of as - welded joints . When the best fit curve is extrapolated to Kw ...
... joints [ 14 ] in which the welds were ground with grinders so as to result in Kw of around 2 . In this case , the joints with ground weld also locate near the lines of as - welded joints . When the best fit curve is extrapolated to Kw ...
Contents
SPECTRAL MODELLING OF WAVES | 1 |
RISK ANALYSIS | 33 |
PROBABILISTIC MODELLING OF WAVES | 99 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis applied ASME assessment base metal bending brittle fracture calculated coefficient corrosion fatigue crack arrestability crack depth crack growth crack tip CTOD curve damage defects deformation dent Det Norske Veritas developed distribution dynamic earthquake effect energy Engineering equation estimated evaluated factor failure fatigue crack Figure fracture mechanics fracture toughness frequency function heat increase initiation inspection Japan maintenance martensitic material maximum mbar measured mechanical properties method notch observed obtained offshore structures OMAE parameters peening performed pipe plastic platform prediction pressure procedure ratio reliability response risers S-N curve safety sea water seismic shielding gas ship shown in Fig simulation single-sided welds specimens spectra spectrum statistical steel plate strain stress range surface Table temperature tensile toughness tubular underwater underwater welding vertical wave height Weibull distribution weld metal welded joints width yield strength yield stress