... higher . The creep values of those test specimen which were plasma cut under water are 100 N / mm2 higher than those of the base mater- ial . The tensile strength values of the test specimen which were flame cut prepared in atmosphere ...
... higher . The creep values of those test specimen which were plasma cut under water are 100 N / mm2 higher than those of the base mater- ial . The tensile strength values of the test specimen which were flame cut prepared in atmosphere ...
Page 377
... higher classes of high strength steels being considered for use in building construction . Unlike mild steel , a reduction in the ability for stress re - distribution due to a higher yield ratio will not provide the sufficient ...
... higher classes of high strength steels being considered for use in building construction . Unlike mild steel , a reduction in the ability for stress re - distribution due to a higher yield ratio will not provide the sufficient ...
Page 186
... higher force ranges . Predictions by the Ralston model and the Edwards - Croasdale model are higher than the measured forces . Edwards and Croasdale Test Data Comparisons of Edwards and Croasdale's test data and model predictions are ...
... higher force ranges . Predictions by the Ralston model and the Edwards - Croasdale model are higher than the measured forces . Edwards and Croasdale Test Data Comparisons of Edwards and Croasdale's test data and model predictions are ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
alloys analysis applied assessment ASTM austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated cathodic protection CGHAZ chord composite crack depth crack growth rates crack propagation CTOD curve defect diameter distribution duplex effect elastic elastomers electrode energy equations experimental failure fatigue crack growth ferrite finite element fracture mechanics fracture toughness geometry grain heat affected zone heat input HSLA steels hydrogen hyperbaric increase interaction Materials Engineering ASME metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic plate predictions preferential corrosion pressure procedure properties ratio region seawater shielding gas shown in Figure simulated solution sour crude oil specimens stainless steel stiffener strain stress concentration stress intensity factor stress range surface Table temperature thermal cycle thickness thread titanium tube tubular joints underwater values weld toe welded joints weldment wire yield strength