... indicated that the problems have arisen due to the local breakdown of the passive film in areas under surface deposits of debris and in tight crevices . These problems have indicated that in order to avoid localised corrosion in ...
... indicated that the problems have arisen due to the local breakdown of the passive film in areas under surface deposits of debris and in tight crevices . These problems have indicated that in order to avoid localised corrosion in ...
Page 499
... indicated that the material had adequate resistance to fracture initiation ; the majority of results , for both the BxB and Bx2B specimens with 1 % local compression , were either maximum load results or high results ( > 0.3mm ) ie ...
... indicated that the material had adequate resistance to fracture initiation ; the majority of results , for both the BxB and Bx2B specimens with 1 % local compression , were either maximum load results or high results ( > 0.3mm ) ie ...
Page 583
... indicated an aspect ratio as high or higher than corresponding data in air . This can be explained in part by considering crack closure measurements in the flat plate specimens . Crack closure measurements were made in most flat plate ...
... indicated an aspect ratio as high or higher than corresponding data in air . This can be explained in part by considering crack closure measurements in the flat plate specimens . Crack closure measurements were made in most flat plate ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
alloys analysis applied assessment ASTM austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated cathodic protection CGHAZ chord composite crack depth crack growth rates crack propagation CTOD curve defect diameter distribution duplex effect elastic elastomers electrode energy equations experimental failure fatigue crack growth ferrite finite element fracture mechanics fracture toughness geometry grain heat affected zone heat input HSLA steels hydrogen hyperbaric increase interaction Materials Engineering ASME metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic plate predictions preferential corrosion pressure procedure properties ratio region seawater shielding gas shown in Figure simulated solution sour crude oil specimens stainless steel stiffener strain stress concentration stress intensity factor stress range surface Table temperature thermal cycle thickness thread titanium tube tubular joints underwater values weld toe welded joints weldment wire yield strength