Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-4American Society of Mechanical Engineers, 1992 - Arctic regions |
From inside the book
Results 1-3 of 91
Page 41
Seven wide plate test specimens ( 406 mm x 1520 mm x 50 mm ) , each containing an EDM notch placed in the HAZ along the length of the weld ( 406 mm ) were fatigue loaded in four point bending at -30 ° C . The notch was positioned so ...
Seven wide plate test specimens ( 406 mm x 1520 mm x 50 mm ) , each containing an EDM notch placed in the HAZ along the length of the weld ( 406 mm ) were fatigue loaded in four point bending at -30 ° C . The notch was positioned so ...
Page 172
Steel Notch Sensitivity was AISI 4140 Steel . Pultruded GRP Rod 6.6 x 10o pet of 30 x 10 ° psi Tensile properties Modulus of Elasticity Tensile Strength Poison's Ratio kuva Poison's Ratio 42 Notch sensitivity obtained by comparing ...
Steel Notch Sensitivity was AISI 4140 Steel . Pultruded GRP Rod 6.6 x 10o pet of 30 x 10 ° psi Tensile properties Modulus of Elasticity Tensile Strength Poison's Ratio kuva Poison's Ratio 42 Notch sensitivity obtained by comparing ...
Page 491
21 Unsafe 81 21 Notch Notch -Kp = f ( Lp ) Safe 20 20 500 600 x ( Lro kr ) L = L , max 700 700 Double stiffener Single stiffener 2c - 50 ( or 20 ) 0.2 Sow cut ( Surloo notch ) 05 3 20-40 or 1201 ( Through thickreu notch ) ( mm ) 1.0 Le ...
21 Unsafe 81 21 Notch Notch -Kp = f ( Lp ) Safe 20 20 500 600 x ( Lro kr ) L = L , max 700 700 Double stiffener Single stiffener 2c - 50 ( or 20 ) 0.2 Sow cut ( Surloo notch ) 05 3 20-40 or 1201 ( Through thickreu notch ) ( mm ) 1.0 Le ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Kapadia Y Adonyi J D Defilippi and W F Domis | 73 |
Copyright | |
36 other sections not shown
Other editions - View all
Common terms and phrases
addition alloys analysis applied assessment axial base base metal behaviour bending calculated carried compared composite considered corrosion crack growth CTOD curve cycles defect depth determined distribution effect element energy Engineering equations estimate experimental factor failure fatigue crack Figure fracture function geometry grain hardness heat higher increase indicated initiation input interaction joint length limit load material mean measured mechanical method microstructure notch observed obtained occur offshore parameters performed pipe plastic plate predictions present pressure probability procedure produced properties range ratio region reported Research seal seawater shown shows significant solution specimens steel strain stress stress intensity structures surface Table temperature tensile thickness thread toughness tubular joints values weld metal wire yield strength zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-4 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1992 |
| Export Citation | BiBTeX EndNote RefMan |