The answer may be derived from the stress and strain analysis in the necked region of a tensile specimen . ... Examination of the specimens suggests that cracks were developed when the a / R ratio was about 1 , where a is the radius of ...
The answer may be derived from the stress and strain analysis in the necked region of a tensile specimen . ... Examination of the specimens suggests that cracks were developed when the a / R ratio was about 1 , where a is the radius of ...
Page 145
PARAMETERS VALUES A detailed analysis of all specimens revealed that except the specimens 1.5 and 1.6 , which presented macrocracks observed at low magnifications , i.e .. 50x or 100x , all specimens 1 ( reference specimen ) , 1.1 , 1.2 ...
PARAMETERS VALUES A detailed analysis of all specimens revealed that except the specimens 1.5 and 1.6 , which presented macrocracks observed at low magnifications , i.e .. 50x or 100x , all specimens 1 ( reference specimen ) , 1.1 , 1.2 ...
Page 583
These readings indicate that crack closure effects had relatively little effect on the behaviour of the free corrosion specimens , but a very significant effect on the cathodically protected specimen . For the case of free corrosion ...
These readings indicate that crack closure effects had relatively little effect on the behaviour of the free corrosion specimens , but a very significant effect on the cathodically protected specimen . For the case of free corrosion ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Kapadia Y Adonyi J D Defilippi and W F Domis | 73 |
Copyright | |
36 other sections not shown
Other editions - View all
Common terms and phrases
addition alloys analysis applied assessment axial base base metal behaviour bending calculated carried compared composite considered corrosion crack growth CTOD curve cycles defect depth determined distribution effect element energy Engineering equations estimate experimental factor failure fatigue crack Figure fracture function geometry grain hardness heat higher increase indicated initiation input interaction joint length limit load material mean measured mechanical method microstructure notch observed obtained occur offshore parameters performed pipe plastic plate predictions present pressure probability procedure produced properties range ratio region reported Research seal seawater shown shows significant solution specimens steel strain stress stress intensity structures surface Table temperature tensile thickness thread toughness tubular joints values weld metal wire yield strength zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-4 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1992 |
| Export Citation | BiBTeX EndNote RefMan |