Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-4American Society of Mechanical Engineers, 1992 - Arctic regions |
From inside the book
Results 1-3 of 76
Page 215
To create adequate strain life curves , a test program of 60 specimens was conducted . The aim of the testing was to establish strain - life curves and discover the effects of temperature , R - value ( mean strain ) , and pad ...
To create adequate strain life curves , a test program of 60 specimens was conducted . The aim of the testing was to establish strain - life curves and discover the effects of temperature , R - value ( mean strain ) , and pad ...
Page 338
Tests 30 and 31 correspond to the same strain ratio as Tests 03 and 09 , but were done a lower strain rates . 2 100 09 03 10 50 60 100 30 2 5 10 20 NEAN PRESSURE kPa Figure 6 20 Vertical stress o , versus mean pressure p , for dry ...
Tests 30 and 31 correspond to the same strain ratio as Tests 03 and 09 , but were done a lower strain rates . 2 100 09 03 10 50 60 100 30 2 5 10 20 NEAN PRESSURE kPa Figure 6 20 Vertical stress o , versus mean pressure p , for dry ...
Page 405
This feature is less pronounced in loose sands since the angle of shear resistance in plane strain does not differ from triaxial conventional tests . Alcantarino , C.A. ( 1986 ) " Design and construction of a plane strain apparatus ...
This feature is less pronounced in loose sands since the angle of shear resistance in plane strain does not differ from triaxial conventional tests . Alcantarino , C.A. ( 1986 ) " Design and construction of a plane strain apparatus ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Kapadia Y Adonyi J D Defilippi and W F Domis | 73 |
Copyright | |
36 other sections not shown
Other editions - View all
Common terms and phrases
addition alloys analysis applied assessment axial base base metal behaviour bending calculated carried compared composite considered corrosion crack growth CTOD curve cycles defect depth determined distribution effect element energy Engineering equations estimate experimental factor failure fatigue crack Figure fracture function geometry grain hardness heat higher increase indicated initiation input interaction joint length limit load material mean measured mechanical method microstructure notch observed obtained occur offshore parameters performed pipe plastic plate predictions present pressure probability procedure produced properties range ratio region reported Research seal seawater shown shows significant solution specimens steel strain stress stress intensity structures surface Table temperature tensile thickness thread toughness tubular joints values weld metal wire yield strength zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-4 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1992 |
| Export Citation | BiBTeX EndNote RefMan |