... temperatures . Low temperature sealing historically has not been a critical factor in performance of downhole equipment . However , with the advent of some new completion practices low temperature performance is taking on a new ...
... temperatures . Low temperature sealing historically has not been a critical factor in performance of downhole equipment . However , with the advent of some new completion practices low temperature performance is taking on a new ...
Page 232
... temperatures are raised to some level above the crystallization temperature . THERMAL STIFFENING There is a more direct effect of lowering temperatures which cause increased stiffness of a polymer just as soon as thermal equilibrium is ...
... temperatures are raised to some level above the crystallization temperature . THERMAL STIFFENING There is a more direct effect of lowering temperatures which cause increased stiffness of a polymer just as soon as thermal equilibrium is ...
Page 54
the ambient temperature decreases across other lower temperature boundaries . Decreasing the ambient temperature from -5 ° C to -15 ° C does not produce the same proportionate benefits as decreasing the ambient temperature from -15 ° C ...
the ambient temperature decreases across other lower temperature boundaries . Decreasing the ambient temperature from -5 ° C to -15 ° C does not produce the same proportionate benefits as decreasing the ambient temperature from -15 ° C ...
Contents
WELD METAL AND HAZ PROPERTIES | 1 |
ADVANCES IN STEEL AND WELDING | 65 |
Development of HSLA Steel With 80Ksi Yield Strength for Offshore Tubular Applications | 73 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
alloys analysis applied assessment ASTM austenite axial load base metal behaviour bending bolt bolted joint brace brittle calculated cathodic protection CGHAZ chord composite crack depth crack growth rates crack propagation CTOD curve defect diameter distribution duplex effect elastic elastomers electrode energy equations experimental failure fatigue crack growth ferrite finite element fracture mechanics fracture toughness geometry grain heat affected zone heat input HSLA steels hydrogen hyperbaric increase interaction Materials Engineering ASME metal yield strength method microstructure nitrogen notch obtained Offshore Structures OMAE parameters pipe plastic plate predictions preferential corrosion pressure procedure properties ratio region seawater shielding gas shown in Figure simulated solution sour crude oil specimens stainless steel stiffener strain stress concentration stress intensity factor stress range surface Table temperature thermal cycle thickness thread titanium tube tubular joints underwater values weld toe welded joints weldment wire yield strength