Ceramography: Preparation and Analysis of Ceramic MicrostructuresCeramography provides detailed instructions on how to saw, mount, grind, polish, etch, examine, interpret and measure ceramic microstructures. This new book includes an atlas of ceramic microstructures, quantitative microstructural example problems with solutions, properties and data tables specific to ceramic microstructures, more than 100 original photographs and illustrations, and numerous practical tips and tricks of the trade. An excellent reference guide for technicians in quality control and R&D, process engineers in ceramic manufacturing, and their counterparts in engineering firms, national laboratories, research institutes, and universities. |
From inside the book
Results 1-3 of 13
Page 6
... furnaces Fume hood for chemical etching and encapsulation removal , storage cabinets for solvents and chemicals , gas - fired furnace Electron microscopes , castable - resin mounting , some furnaces Etching furnace , sputter coater X ...
... furnaces Fume hood for chemical etching and encapsulation removal , storage cabinets for solvents and chemicals , gas - fired furnace Electron microscopes , castable - resin mounting , some furnaces Etching furnace , sputter coater X ...
Page 15
... furnace . A sheet of platinum foil beneath the green compacts may be desirable , if contamination from the refractory is a problem . Heat the furnace slowly to the sintering temperature , typically ~ 300 K below the melting temperature ...
... furnace . A sheet of platinum foil beneath the green compacts may be desirable , if contamination from the refractory is a problem . Heat the furnace slowly to the sintering temperature , typically ~ 300 K below the melting temperature ...
Page 53
... furnace with a clean interior and clean heating elements . Close the furnace and start the purge gas flow or vacuum pump , if applicable . Heat the furnace to the etching tem- perature , approximately 1500 ° C for alumina and fully ...
... furnace with a clean interior and clean heating elements . Close the furnace and start the purge gas flow or vacuum pump , if applicable . Heat the furnace to the etching tem- perature , approximately 1500 ° C for alumina and fully ...
Contents
Ceramic Fabrication | 9 |
Sawing and Mounting | 19 |
Grinding and Polishing | 35 |
Copyright | |
16 other sections not shown
Other editions - View all
Ceramography: Preparation and Analysis of Ceramic Microstructures Richard E. Chinn Limited preview - 2002 |
Common terms and phrases
abrasive acid acoustic Al2O alumina analysis applied approximately ASTM beam binary carbide ceramics ceramographic Chapter clean coating color composition compression contain contrast crack crystal described diameter diamond direction edge electric electron electron microscope Engineered equipment field fracture furnace glass grain boundaries grain size gray levels grinding Handbook hardness heat illumination image analyzer indentation interference layer length lens less light liquid load magnification Materials mean measurement Metallographic Metals method microscope microstructure mold mounting objects optical original particles phase polarized polishing pores porosity Practice preparation pressure procedures properties reflected refractive relief removed require resin Scanning shape shown in Fig Silicon sintering slide Source specimen sputter stage standard step structure Subroutine surface Table Testing thermally etched thin section TiO2 tion toughness transmitted USA Telephone usually viewed volume