Treatise on Materials Science and TechnologyHerbert Herman, Minoru Tomozawa, Robert H. Doremus |
From inside the book
Results 1-3 of 30
Page 161
... coefficient do not reflect particular local structural states but are obtained as an average of the overall structure of a glass . Accord- ingly , these properties are mainly determined by the oxide com- position of the glass . Dislich ...
... coefficient do not reflect particular local structural states but are obtained as an average of the overall structure of a glass . Accord- ingly , these properties are mainly determined by the oxide com- position of the glass . Dislich ...
Page 215
... coefficients from the regres- sion ( Draper and Smith , 1966 ) . The mean logt values for Pyrex glass in Table VII ... coefficient R2 www3 34 0.805 35 0.869 36 0.917 37 0.944 tion of the spread ( standard deviation ) of logt FRACTURE ...
... coefficients from the regres- sion ( Draper and Smith , 1966 ) . The mean logt values for Pyrex glass in Table VII ... coefficient R2 www3 34 0.805 35 0.869 36 0.917 37 0.944 tion of the spread ( standard deviation ) of logt FRACTURE ...
Page 256
... coefficient over 25 ° C to 300 ° C . It is shown in Section IV , I that because of the steep rise in the expansion coefficient , the use of conventional 25-300 ° C values can often lead to erroneous results . Thermal expansion curves of ...
... coefficient over 25 ° C to 300 ° C . It is shown in Section IV , I that because of the steep rise in the expansion coefficient , the use of conventional 25-300 ° C values can often lead to erroneous results . Thermal expansion curves of ...
Contents
Water in Glass | 75 |
Applications | 121 |
Gel Method for Making Glass | 129 |
Copyright | |
15 other sections not shown
Common terms and phrases
acid activation energy adsorption alkali alkoxide alkoxide method alkoxide solution annealing point atoms autoclave Bartholomew bead seal BK7 glass bond borosilicate borosilicate glass bulk glass calculated Ceram Chem chemical components crack propagation crack tip crystals curve density dependence desorption diameter distribution Dunken effect elastic energy equation etching experimental failure film flaws fused silica geometry glass fibers glass surface H₂O heating Hillig hydrated hydrolysis hydrosilicate increase ions layer liquid load material measured melting metal alkoxides mole Na2O Non-Cryst OH groups Pavelchek and Doremus Phys powders Pyrex ratio reaction refractive index Rekhson samples sandwich seal Section set point shown in Fig shows silicate glasses SiO2 SiO2 glass soda-lime glass Solids spectra static fatigue strain stress release structure Table technique temperature tensile stress thermal expansion TiO2 tion tip radius values vapor Varshneya velocity viscosity water content Wiederhorn Young's modulus ZrO2