Treatise on Materials Science and TechnologyHerbert Herman, Minoru Tomozawa, Robert H. Doremus |
From inside the book
Results 1-3 of 28
Page 62
... components of a glass plays a determining role . In Table V oxides , elements , and nonoxide components of different glasses are listed . These components have only slight solubility in water or con- centrated acids or bases at room ...
... components of a glass plays a determining role . In Table V oxides , elements , and nonoxide components of different glasses are listed . These components have only slight solubility in water or con- centrated acids or bases at room ...
Page 63
... Components IN DIFFERENT INORGANIC MEDIA AT ROOM TEMPERATURE a Medium Glass components H2O HF ( 47 % ) H2SO4 ( 96 % ) HNO3 ( 70 % ) HCl ( 37 % ) H3PO4 ( 85 % ) NaOH , KOH ( 50 % ) BeO , MgO , ( SiO2 ) , SnO , CeO2 , TiO2 , ZrO2 , Si , Ge ...
... Components IN DIFFERENT INORGANIC MEDIA AT ROOM TEMPERATURE a Medium Glass components H2O HF ( 47 % ) H2SO4 ( 96 % ) HNO3 ( 70 % ) HCl ( 37 % ) H3PO4 ( 85 % ) NaOH , KOH ( 50 % ) BeO , MgO , ( SiO2 ) , SnO , CeO2 , TiO2 , ZrO2 , Si , Ge ...
Page 245
... components vanishes ( e.g. , if one examines σ1 σ2 while ap- proaching the surface , the component normal to the surface van- ishes ) . → The second limitation is also quite severe . It generally STRESSES IN GLASS - TO - METAL SEALS 245.
... components vanishes ( e.g. , if one examines σ1 σ2 while ap- proaching the surface , the component normal to the surface van- ishes ) . → The second limitation is also quite severe . It generally STRESSES IN GLASS - TO - METAL SEALS 245.
Contents
Water in Glass | 75 |
Applications | 121 |
Gel Method for Making Glass | 129 |
Copyright | |
15 other sections not shown
Common terms and phrases
acid activation energy adsorption alkali alkoxide alkoxide method alkoxide solution annealing point atoms autoclave Bartholomew bead seal BK7 glass bond borosilicate borosilicate glass bulk glass calculated Ceram Chem chemical components crack propagation crack tip crystals curve density dependence desorption diameter distribution Dunken effect elastic energy equation etching experimental failure film flaws fused silica geometry glass fibers glass surface H₂O heating Hillig hydrated hydrolysis hydrosilicate increase ions layer liquid load material measured melting metal alkoxides mole Na2O Non-Cryst OH groups Pavelchek and Doremus Phys powders Pyrex ratio reaction refractive index Rekhson samples sandwich seal Section set point shown in Fig shows silicate glasses SiO2 SiO2 glass soda-lime glass Solids spectra static fatigue strain stress release structure Table technique temperature tensile stress thermal expansion TiO2 tion tip radius values vapor Varshneya velocity viscosity water content Wiederhorn Young's modulus ZrO2