... fibers by heating at 800 ° C . No fracture or crack occurred when the fibrous gels were introduced into the furnace at high temperatures . • Kamiya et al . ( 1976 ) produced glass fibers of composition 30 % Al2O3 70 % SiO2 in weight ...
... fibers by heating at 800 ° C . No fracture or crack occurred when the fibrous gels were introduced into the furnace at high temperatures . • Kamiya et al . ( 1976 ) produced glass fibers of composition 30 % Al2O3 70 % SiO2 in weight ...
Page 150
... fibers were drawn from the solutions . The resultant fibrous gels were heated at 500-700 ° C to convert them into glass fibers . Thus fibers of compositions 7 % ZrO2 93 % SiO2 , 26 % ZrO2 74 % SiO2 , 33 % ZrO2 67 % SiO2 , 48 % ZrO2 52 ...
... fibers were drawn from the solutions . The resultant fibrous gels were heated at 500-700 ° C to convert them into glass fibers . Thus fibers of compositions 7 % ZrO2 93 % SiO2 , 26 % ZrO2 74 % SiO2 , 33 % ZrO2 67 % SiO2 , 48 % ZrO2 52 ...
Page 151
... fiber drawing . Fibers were drawn and heated to the final products . Yajima et al . ( 1975 , 1976 ) produced silicon carbide fibers from a silane . This is briefly described here because the inorganic fibers were made from organic ...
... fiber drawing . Fibers were drawn and heated to the final products . Yajima et al . ( 1975 , 1976 ) produced silicon carbide fibers from a silane . This is briefly described here because the inorganic fibers were made from organic ...
Contents
Water in Glass | 75 |
Applications | 121 |
Gel Method for Making Glass | 129 |
Copyright | |
15 other sections not shown
Common terms and phrases
acid activation energy adsorption alkali alkoxide alkoxide method alkoxide solution annealing point atoms autoclave Bartholomew bead seal BK7 glass bond borosilicate borosilicate glass bulk glass calculated Ceram Chem chemical components crack propagation crack tip crystals curve density dependence desorption diameter distribution Dunken effect elastic energy equation etching experimental failure film flaws fused silica geometry glass fibers glass surface H₂O heating Hillig hydrated hydrolysis hydrosilicate increase ions layer liquid load material measured melting metal alkoxides mole Na2O Non-Cryst OH groups Pavelchek and Doremus Phys powders Pyrex ratio reaction refractive index Rekhson samples sandwich seal Section set point shown in Fig shows silicate glasses SiO2 SiO2 glass soda-lime glass Solids spectra static fatigue strain stress release structure Table technique temperature tensile stress thermal expansion TiO2 tion tip radius values vapor Varshneya velocity viscosity water content Wiederhorn Young's modulus ZrO2