Treatise on Materials Science and TechnologyHerbert Herman, Minoru Tomozawa, Robert H. Doremus |
From inside the book
Results 1-3 of 27
Page 80
... hydrated directly in liquid water under the autoclave conditions used for steam treatment . A far larger number of glasses can be hydrated in the liquid phase in the autoclave in solutions containing alkali - metal ion salts or under ...
... hydrated directly in liquid water under the autoclave conditions used for steam treatment . A far larger number of glasses can be hydrated in the liquid phase in the autoclave in solutions containing alkali - metal ion salts or under ...
Page 81
... HYDRATED RIBBON Soda profile by chemical etching technique . Hydrosilicate glass A auto- claved 16 hr at 270 ° C in Pb ( NO3 ) / HNO , solution . ranging from 5 to 150 g in 100 ml results in leached and crystallized surfaces . However ...
... HYDRATED RIBBON Soda profile by chemical etching technique . Hydrosilicate glass A auto- claved 16 hr at 270 ° C in Pb ( NO3 ) / HNO , solution . ranging from 5 to 150 g in 100 ml results in leached and crystallized surfaces . However ...
Page 83
... hydrated 1 mm hydrated 1 mm hydrated 1 mm hydrated 0.6 % Al2O3 77.6 % SiO2 , 21.2 % Na2O , 1.2 % Al2O3 0 140 2 160 16 1010 41.0 1 mm hydrated 14.1 1 mm hydrated a " For composition of glass A , see text . Other glass compositions are in ...
... hydrated 1 mm hydrated 1 mm hydrated 1 mm hydrated 0.6 % Al2O3 77.6 % SiO2 , 21.2 % Na2O , 1.2 % Al2O3 0 140 2 160 16 1010 41.0 1 mm hydrated 14.1 1 mm hydrated a " For composition of glass A , see text . Other glass compositions are in ...
Contents
Water in Glass | 75 |
Applications | 121 |
Gel Method for Making Glass | 129 |
Copyright | |
15 other sections not shown
Common terms and phrases
acid activation energy adsorption alkali alkoxide alkoxide method alkoxide solution annealing point atoms autoclave Bartholomew bead seal BK7 glass bond borosilicate borosilicate glass bulk glass calculated Ceram Chem chemical components crack propagation crack tip crystals curve density dependence desorption diameter distribution Dunken effect elastic energy equation etching experimental failure film flaws fused silica geometry glass fibers glass surface H₂O heating Hillig hydrated hydrolysis hydrosilicate increase ions layer liquid load material measured melting metal alkoxides mole Na2O Non-Cryst OH groups Pavelchek and Doremus Phys powders Pyrex ratio reaction refractive index Rekhson samples sandwich seal Section set point shown in Fig shows silicate glasses SiO2 SiO2 glass soda-lime glass Solids spectra static fatigue strain stress release structure Table technique temperature tensile stress thermal expansion TiO2 tion tip radius values vapor Varshneya velocity viscosity water content Wiederhorn Young's modulus ZrO2