Treatise on Materials Science and TechnologyHerbert Herman, Minoru Tomozawa, Robert H. Doremus |
From inside the book
Results 1-3 of 48
Page 97
... phase decreased corrosion . Furthermore , corrosion occurred faster in the steam phase than in the liquid phase , with unannealed samples corroding faster than annealed . Friedman and Long ( 1976 ) hydrated obsidian samples of different ...
... phase decreased corrosion . Furthermore , corrosion occurred faster in the steam phase than in the liquid phase , with unannealed samples corroding faster than annealed . Friedman and Long ( 1976 ) hydrated obsidian samples of different ...
Page 108
... phase separation occurs by nucleation and growth ; the morphology is that of discrete particles in a continuous matrix . In the unstable region , phase separation is characterized by an interconnected microstruc- ture developed by ...
... phase separation occurs by nucleation and growth ; the morphology is that of discrete particles in a continuous matrix . In the unstable region , phase separation is characterized by an interconnected microstruc- ture developed by ...
Page 142
... phase precipitating on heating , and remains unchanged in phase up to 1000 ° C . It should be noted that anatase is a metastable phase at these temperatures . The rutile phase is observed only for the compositions containing more than ...
... phase precipitating on heating , and remains unchanged in phase up to 1000 ° C . It should be noted that anatase is a metastable phase at these temperatures . The rutile phase is observed only for the compositions containing more than ...
Contents
Water in Glass | 75 |
Applications | 121 |
Gel Method for Making Glass | 129 |
Copyright | |
15 other sections not shown
Common terms and phrases
acid activation energy adsorption alkali alkoxide alkoxide method alkoxide solution annealing point atoms autoclave Bartholomew bead seal BK7 glass bond borosilicate borosilicate glass bulk glass calculated Ceram Chem chemical components crack propagation crack tip crystals curve density dependence desorption diameter distribution Dunken effect elastic energy equation etching experimental failure film flaws fused silica geometry glass fibers glass surface H₂O heating Hillig hydrated hydrolysis hydrosilicate increase ions layer liquid load material measured melting metal alkoxides mole Na2O Non-Cryst OH groups Pavelchek and Doremus Phys powders Pyrex ratio reaction refractive index Rekhson samples sandwich seal Section set point shown in Fig shows silicate glasses SiO2 SiO2 glass soda-lime glass Solids spectra static fatigue strain stress release structure Table technique temperature tensile stress thermal expansion TiO2 tion tip radius values vapor Varshneya velocity viscosity water content Wiederhorn Young's modulus ZrO2