Treatise on Materials Science and TechnologyHerbert Herman, Minoru Tomozawa, Robert H. Doremus |
From inside the book
Results 1-3 of 14
Page 138
... removal is not easy , although the OH content is slightly higher in alkoxy - derived glasses . Figure 6 shows the infrared spectra for the gel of SiO2 composition after heating at various temperatures ( Kamiya et al . , 1978 ) . The ...
... removal is not easy , although the OH content is slightly higher in alkoxy - derived glasses . Figure 6 shows the infrared spectra for the gel of SiO2 composition after heating at various temperatures ( Kamiya et al . , 1978 ) . The ...
Page 155
... removed from the sheet , and converted to a glass film by heating . An appropriate selection of plastics for support and surface treatment facilitated the removal of the film from the supporting sheet , giving clear indepen- dent films ...
... removed from the sheet , and converted to a glass film by heating . An appropriate selection of plastics for support and surface treatment facilitated the removal of the film from the supporting sheet , giving clear indepen- dent films ...
Page 194
... removed ( Taylor , 1949 ; Neely and MacKenzie , 1968 ) . This deformation in fused silica is apparently a ... removal of the load . 3. Viscous - the uniform nonrecoverable flow of a liquid or amorphous solid subjected to a ...
... removed ( Taylor , 1949 ; Neely and MacKenzie , 1968 ) . This deformation in fused silica is apparently a ... removal of the load . 3. Viscous - the uniform nonrecoverable flow of a liquid or amorphous solid subjected to a ...
Contents
Water in Glass | 75 |
Applications | 121 |
Gel Method for Making Glass | 129 |
Copyright | |
15 other sections not shown
Common terms and phrases
acid activation energy adsorption alkali alkoxide alkoxide method alkoxide solution annealing point atoms autoclave Bartholomew bead seal BK7 glass bond borosilicate borosilicate glass bulk glass calculated Ceram Chem chemical components crack propagation crack tip crystals curve density dependence desorption diameter distribution Dunken effect elastic energy equation etching experimental failure film flaws fused silica geometry glass fibers glass surface H₂O heating Hillig hydrated hydrolysis hydrosilicate increase ions layer liquid load material measured melting metal alkoxides mole Na2O Non-Cryst OH groups Pavelchek and Doremus Phys powders Pyrex ratio reaction refractive index Rekhson samples sandwich seal Section set point shown in Fig shows silicate glasses SiO2 SiO2 glass soda-lime glass Solids spectra static fatigue strain stress release structure Table technique temperature tensile stress thermal expansion TiO2 tion tip radius values vapor Varshneya velocity viscosity water content Wiederhorn Young's modulus ZrO2