Treatise on Materials Science and TechnologyHerbert Herman, Minoru Tomozawa, Robert H. Doremus |
From inside the book
Results 1-3 of 58
Page 62
... solution volume , the ratio of the surface area of the glass to the solution volume plays a decisive role ( Ethridge et al . , 1979 ) . Dynamic conditions , in which the solution is constantly renewed , avoid this influence of changing ...
... solution volume , the ratio of the surface area of the glass to the solution volume plays a decisive role ( Ethridge et al . , 1979 ) . Dynamic conditions , in which the solution is constantly renewed , avoid this influence of changing ...
Page 64
Herbert Herman, Minoru Tomozawa, Robert H. Doremus. alkaline solutions ( pH ≤8 ) or GeO2 glasses in HNO3 solution . The dominant reaction step is the partial leaching of glass components with the formation of a gel - like layer of ...
Herbert Herman, Minoru Tomozawa, Robert H. Doremus. alkaline solutions ( pH ≤8 ) or GeO2 glasses in HNO3 solution . The dominant reaction step is the partial leaching of glass components with the formation of a gel - like layer of ...
Page 136
... solution has been diluted with ethyl alcohol in order to hydrolyze the solution in a clear state without undesirable inhomogenous precipitation of hydrolyzed par- ticulate product . The alkoxide solutions with no addition of water and ...
... solution has been diluted with ethyl alcohol in order to hydrolyze the solution in a clear state without undesirable inhomogenous precipitation of hydrolyzed par- ticulate product . The alkoxide solutions with no addition of water and ...
Contents
Water in Glass | 75 |
Applications | 121 |
Gel Method for Making Glass | 129 |
Copyright | |
15 other sections not shown
Common terms and phrases
acid activation energy adsorption alkali alkoxide alkoxide method alkoxide solution annealing point atoms autoclave Bartholomew bead seal BK7 glass bond borosilicate borosilicate glass bulk glass calculated Ceram Chem chemical components crack propagation crack tip crystals curve density dependence desorption diameter distribution Dunken effect elastic energy equation etching experimental failure film flaws fused silica geometry glass fibers glass surface H₂O heating Hillig hydrated hydrolysis hydrosilicate increase ions layer liquid load material measured melting metal alkoxides mole Na2O Non-Cryst OH groups Pavelchek and Doremus Phys powders Pyrex ratio reaction refractive index Rekhson samples sandwich seal Section set point shown in Fig shows silicate glasses SiO2 SiO2 glass soda-lime glass Solids spectra static fatigue strain stress release structure Table technique temperature tensile stress thermal expansion TiO2 tion tip radius values vapor Varshneya velocity viscosity water content Wiederhorn Young's modulus ZrO2