Treatise on Materials Science and TechnologyHerbert Herman, Minoru Tomozawa, Robert H. Doremus |
From inside the book
Results 1-3 of 22
Page 191
... suggests that the minimum tip radius for fracture is about ten atomic distances ; if the tip radius is smaller than ... suggested that these equations must be modified for non- linear elastic or plastic behavior at high stresses . The ...
... suggests that the minimum tip radius for fracture is about ten atomic distances ; if the tip radius is smaller than ... suggested that these equations must be modified for non- linear elastic or plastic behavior at high stresses . The ...
Page 215
... suggested , but for the present these four are adequate . Over the stress ranges studied experimentally it is often difficult to choose from among Eqs . ( 34 ) – ( 37 ) , yet if they are extrapolated to times of a few years , the sample ...
... suggested , but for the present these four are adequate . Over the stress ranges studied experimentally it is often difficult to choose from among Eqs . ( 34 ) – ( 37 ) , yet if they are extrapolated to times of a few years , the sample ...
Page 233
... suggest that the glass itself can act as a source of water at low humidities . The crack velocity - load relation for soda - lime glass is not much influenced by the pH of a contacting solution in the pH range from about 1 to 13 ...
... suggest that the glass itself can act as a source of water at low humidities . The crack velocity - load relation for soda - lime glass is not much influenced by the pH of a contacting solution in the pH range from about 1 to 13 ...
Contents
Water in Glass | 75 |
Applications | 121 |
Gel Method for Making Glass | 129 |
Copyright | |
15 other sections not shown
Common terms and phrases
acid activation energy adsorption alkali alkoxide alkoxide method alkoxide solution annealing point atoms autoclave Bartholomew bead seal BK7 glass bond borosilicate borosilicate glass bulk glass calculated Ceram Chem chemical components crack propagation crack tip crystals curve density dependence desorption diameter distribution Dunken effect elastic energy equation etching experimental failure film flaws fused silica geometry glass fibers glass surface H₂O heating Hillig hydrated hydrolysis hydrosilicate increase ions layer liquid load material measured melting metal alkoxides mole Na2O Non-Cryst OH groups Pavelchek and Doremus Phys powders Pyrex ratio reaction refractive index Rekhson samples sandwich seal Section set point shown in Fig shows silicate glasses SiO2 SiO2 glass soda-lime glass Solids spectra static fatigue strain stress release structure Table technique temperature tensile stress thermal expansion TiO2 tion tip radius values vapor Varshneya velocity viscosity water content Wiederhorn Young's modulus ZrO2