Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 51
Page 401
... achieved using a C - 1.7 % Mn wire together with a fully basic flux . The consumable combination must have the capability of consistently meeting these minimum mechanical property requirements together with providing resistance to cold ...
... achieved using a C - 1.7 % Mn wire together with a fully basic flux . The consumable combination must have the capability of consistently meeting these minimum mechanical property requirements together with providing resistance to cold ...
Page 489
... achieved . This approach , however , can be challenged on the grounds that it is extremely difficult to achieve consistently high toughness levels in fabrications welds . Therefore , there is no incentive to consider weld metal ...
... achieved . This approach , however , can be challenged on the grounds that it is extremely difficult to achieve consistently high toughness levels in fabrications welds . Therefore , there is no incentive to consider weld metal ...
Page 589
... achieved by utilising a suitable dispersion of Ti , Nb ( N , C ) particles to confer austenite grain size control during slab reheating , and subsequent achievement of a fine recrystallised austenite grain size prior to finish rolling ...
... achieved by utilising a suitable dispersion of Ti , Nb ( N , C ) particles to confer austenite grain size control during slab reheating , and subsequent achievement of a fine recrystallised austenite grain size prior to finish rolling ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone