Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 41
Page 627
... Carbon Steels ܘܣܘ Brine Electrolyte Deaerated O Not Deaerated O O 0.1 0.2 0.3 0.4 0.5 Carbon % Fig . 6 Corrosion rate vs. carbon content of low residual plain carbon steels in brine . 30 25 30 Brine Electrolyte ( Not Deaerated ) 25 O ...
... Carbon Steels ܘܣܘ Brine Electrolyte Deaerated O Not Deaerated O O 0.1 0.2 0.3 0.4 0.5 Carbon % Fig . 6 Corrosion rate vs. carbon content of low residual plain carbon steels in brine . 30 25 30 Brine Electrolyte ( Not Deaerated ) 25 O ...
Page 628
... steels of lower carbon composition . The corrosion rates were essentially invariant for the four steels examined ( 0.1 0.4 % C ( alloyed with 4 % Cr ) and the carbon content did not appear to affect the corrosion rate . - Corrosion ...
... steels of lower carbon composition . The corrosion rates were essentially invariant for the four steels examined ( 0.1 0.4 % C ( alloyed with 4 % Cr ) and the carbon content did not appear to affect the corrosion rate . - Corrosion ...
Page 629
... carbon steel in sour brine . 5 1 2 3 Cobalt % Fig.12 Corrosion rate vs. cobalt content for various grades in sour brine environment . It is Cobalt alloved low residual Steels . Figure 11 compares the dis - solution rates of 2 % Co ...
... carbon steel in sour brine . 5 1 2 3 Cobalt % Fig.12 Corrosion rate vs. cobalt content for various grades in sour brine environment . It is Cobalt alloved low residual Steels . Figure 11 compares the dis - solution rates of 2 % Co ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone